Stress- and Time-Dependent Formation of Self-Lubricating In Situ Carbon (SLIC) Films on Catalytically-Active Noble Alloys

Figure 5 from Morgan R. Jones et al. Stress- and Time-Dependent Formation of Self-Lubricating In Situ Carbon (SLIC) Films on Catalytically-Active Noble Alloys: Tribofilm formation as a function of number of cycles as determined from the nanoscale experiments. (a) Intermittent-contact mode topography images (3 µm × 3 µm area) of the contact region at a contact pressure of 1.2 GPa after 0 cycles, 500 cycles, 1000 cycles, 2000 cycles, 3000 cycles, and 4000 cycles. (b) Tribofilm volume as a function of cycles for contact pressures up to 3.1 GPa. For all P, tribofilm volume increased asymptotically to a steady-state value at large numbers of cycles. NANOSENSORS Diamond Coated PointProbe Plus AFM probes DT-CONTR were used for the nanoscale tribology with atomic force microscopy.

Although catalysis is a popular explanation for tribopolymer generation, the interplay of catalysis, mechanochemistry, and electrostatic interactions remain incompletely understood. There is consensus, however, that… Read More »Stress- and Time-Dependent Formation of Self-Lubricating In Situ Carbon (SLIC) Films on Catalytically-Active Noble Alloys